| Feature: | Photodegradable |
|---|---|
| CAS No.: | 9003-56-9 |
| Formula: | (C8h8)N |
| EINECS: | C45h51n3X2 |
| Material: | Acrylonitrile-Butadiene-Styrene Copolymers/ABS |
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier ABS is a terpolymer of three monomers: acrylonitrileA), butadiene (B) and styrene (S). The relative content of the three monomers can be changed at will to make various resins. ABS plastic has the common properties of three components. A makes it resistant to chemical corrosion, heat resistance, and has a certain surface hardness, B makes it have high elasticity and toughness, and S makes it have the processing and molding characteristic of thermoplastics and improve electrical properties. performance. Therefore, ABS plastic is a kind of "tough, hard and rigid" material with easy-to-obtain raw materials, good comprehensive performance, low price and wide range of uses.
| Functional Item | Test condition | test method | test data | data unit | |
| mechanical capacity | tensile strength | 1/8",50mm/min | ASTM D-638 | 510 | kg/cm2 |
| stretch rate | 1/8",50mm/min | ASTM D-638 | 40 | % | |
| bending strength | 1/8",1.3mm/min | ASTM D-790 | 770 | kg/cm2 | |
| flexural modulus | 1/8",1.3mm/min | ASTM D-790 | 25180 | kg/cm2 | |
| IZODimpact strength | 1/8",1.3mm/min | ASTM D-256 | 25 | kg.cm/cm | |
| Rockwell hardness | ASTM D-256 | 112 | R Scale | ||
| thermal properties | heat deflection temperature | 1/8",1.8MPa | ASTM D-648 | 80 | ºC |
| vicat softening point | 1kg | ASTM D-1525 | 99 | ºC | |
| heat of combustion | 1/8" | UL 94 | HB | ||
| physical properties | melt index | 220ºC/10kg | ASTM D-1238 | 15.5 | g/10min |
| specific gravity | 23ºC | ASTM D-792 | 1.045 | ||
| molding shrinkage | ASTM D-955 | 0.5-0.8 | % | ||