| Customization: | Available |
|---|---|
| CAS No.: | 13463-67-7 |
| Formula: | TiO2 |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Titanium dioxide, an inorganic compound, chemical formula for TiO2, is a white solid or powdered amphoteric oxide, molecular weight 79.866, with non-toxic, the best opacity, the best whiteness and brightness, is considered to be the world's best performance of a white pigment. Titanium white has strong adhesion, is not easy to change chemically, and is always white. Widely used in coating, plastic, paper, printing ink, chemical fiber, rubber, cosmetics and other industries. It has a very high melting point and is also used to make refractory glass, glazes, enamel, clay, and high temperature resistant experimental vessels. Titanium dioxide can be extracted from rutile by acid decomposition or obtained from decomposition. Titanium dioxide exists in nature in three allotropic forms: rutile, anatase and plate titanium, in addition to several synthetic crystal forms.
| Property | Company | SR-237 |
| Tio2 content | %≥ | 93.0 |
| Rutile content | %≥ | 97.0 |
| Inorganic coating | Si . Al | |
| Organic treatment | Yes | |
| Loss at 105ºC | %≤ | 0.50 |
| Solution in water | %≤ | 0.5 |
| Residue | %≤ | 0.01 |
| Whiteness | %≥ | 97.0 |
| L Value | ≥ | 98.0 |
| Tint reducing power | %≥ | 180 |
| Oil absorption, g/100g | ≤ | 17-22 |
| PH | 7.0-9.0 | |
| Specific resistance | Ωcm≥ | 5000 |
| Property | Company | SR-2377 |
| Tio2 content | %≥ | 93.0 |
| Rutile content | %≥ | 97.0 |
| Inorganic coating | Zr . Al | |
| Organic treatment | Yes | |
| Loss at 105ºC | %≤ | 0.50 |
| Solution in water | %≤ | 0.5 |
| Residue | %≤ | 0.01 |
| Whiteness | %≥ | 97.0 |
| L Value | ≥ | 98.0 |
| Tint reducing power | %≥ | 180 |
| Oil absorption, g/100g | ≤ | 16-20 |
| PH | 6.5-8.5 | |
| Specific resistance | Ωcm ≥ | 8000 |
| Property | Company | SR-2400 |
| Tio2 content | %≥ | 94.0 |
| Rutile content | %≥ | 97.0 |
| Inorganic coating | Al | |
| Organic treatment | Yes | |
| Loss at 105ºC | %≤ | 0.50 |
| Solution in water | %≤ | 0.5 |
| Residue | %≤ | 0.01 |
| Whiteness | %≥ | 97.0 |
| L Value | ≥ | 98.0 |
| Tint reducing power | %≥ | 185 |
| Oil absorption , g/100g | ≤ | 15-18 |
| PH | 6.5-8.0 | |
| Specific resistance | Ωcm ≥ | 8000 |
| Hydropnobic/half Hydropnobic | ||
| Property | Company | SR-240 |
| Tio2 content | %≥ | 96.0 |
| Rutile content | %≥ | 97.0 |
| Inorganic coating | Al | |
| Organic treatment | Yes | |
| Loss at 105ºC | %≤ | 0.50 |
| Solution in water | %≤ | 0.5 |
| Residue | %≤ | 0.01 |
| Whiteness | %≥ | 97.0 |
| L Value | ≥ | 98.0 |
| Tint reducing power | %≥ | 180 |
| Oil absorption , g/100g | ≤ | 18-21 |
| PH | 6.5-8.0 | |
| Specific resistance | Ωcm ≥ | 8500 |